Effect of Different Annealing Temperatures on Structural, Optical, Morphological and Electrical Properties of Cu - ZnO Thin Films Prepared Using Sol—gel Spin Coating Techniques

Mohana F. Attia

Journal of Materials Science Research and Reviews · pp. 258–282 · Published 1 Jun 2019

10.9734/jmsrr/2019/v2i252

Abstract

In this study, Cu - doped ZnO thin films were prepared at different annealing temperatures from Copper acetate precursor by sol-gel spin coating method for Photocatalytic Applications.  The films were characterized by X-ray diffractometer (XRD), scanning electron microscopy (SEM), and Fourier transform infrared spectroscopy (FTIR).  The obtained powders were annealed under air in the range of  for Cu – ZnO. The surface morphological, structural, electrical and optical properties of the as-deposited ZnO films have been investigated as a function of Cu-doping level.  The thickness of the films was estimated by Fizeau fringes interference method which varied from 195 to 198 nm. The X-ray diffraction analysis indicated that the wurtzite structure was maintained for all samples and copper was successfully doped into ZnO at low TC. However, the formation of monoclinic CuO was observed at higher TC. For Cu – ZnO, the crystallite size increased with the annealing temperature from 15.86 to 24.24 nm. The isotherms obtained were type IV with a hysteresis type H 3, confirming the mesoporous behavior of the catalysts. The surface area was in the range of 35.1 to 8.66 /g. All the prepared catalysts mainly showed two emission regions: a sharp peak in the ultraviolet region and another broad peak in the visible region. The photocatalytic activity was achieved by the degradation of 300 mg/L malachite green (MG) aqueous solution under UV irradiation. The findings showed that the increased annealing of different concentration of Cu doped ZnO with CuO on the surface resulted in highly improved photocatalytic activity. Various optical constants such as absorbance, transmittance of the films have been studied. The values of transmittance are high in the visible and IR region and it is minimum in the UV region. Absorbance decreases with higher percentage of Cu concentration. The band gap of the films varied 3.21 to 3.05 eV. The resistivity gradually decreases with the increase of temperature, which indicates the semiconducting nature of the materials. Resistivity also increases with the increasing doping concentration. The conductivity decreases with the increasing of Cu concentration.

Zinc oxide sol – gel malachite green annealing temperature copper photocatalytic activity resistivity conductivity

References (25)

  1. 1 A comprehensive review of ZnO materials and devices [DOI]
  2. 2 Synthesis and characterization of zinc oxide nanoparticles: application to textiles as UV-absorbers [DOI]
  3. 3 Rare Earth Doped Zinc Oxide Nanophosphor Powder: A Future Material for Solid State Lighting and Solar Cells [DOI]
  4. 4 Sol–gel synthesized zinc oxide nanorods and their structural and optical investigation for optoelectronic application [DOI]
  5. 5 Synthesis and characterization of ZnO–CuO nanocomposites powder by modified perfume spray pyrolysis method and its antimicrobial investigation [DOI]
  6. 6 Equilibrium and kinetic studies of the adsorption of acid blue 9 and Safranin O from aqueous solutions by MgO decked FLG coated Fuller's earth [DOI]
  7. 7 Removal of humic acid from aqueous solution using UV/ZnO nano-photocatalysis and adsorption [DOI]
  8. 8 Synthesis and characterization studies of MgO:CuO nanocrystals by wet-chemical method [DOI]
  9. 9 Structural and optical properties of Co-doped ZnO nanocrystallites prepared by a one-step solution route [DOI]
  10. 10 A facile approach to the synthesis of high-quality NiO nanorods: electrochemical and antibacterial properties [DOI]
  11. 11 Ga-doped ZnO for adsorption of heavy metals from aqueous solution [DOI]
  12. 12 Development of antiproliferative nanohybrid compound with controlled release property using ellagic acid as the active agent [DOI]
  13. 13 A study of magnetic and optical properties of Cu‐doped ZnO [DOI]
  14. 14 Synthesis, characterization and properties of Mn-doped ZnO nanocrystals [DOI]
  15. 15 Structural characterization of “as-deposited” cesium iodide films studied by X-ray diffraction and transmission electron microscopy techniques [DOI]
  16. 16 Strong ultraviolet emission and rectifying behavior of nanocrystalline ZnO films [DOI]
  17. 17 Deep level defect correlated emission and Si diffusion in ZnO:Tb 3+ thin films prepared by pulsed laser deposition [DOI]
  18. 18 Structural, Optical and Luminescence Properties of ZnO Thin Films Prepared by Sol-Gel Spin-Coating Method: Effect of Precursor Concentration [DOI]
  19. 19 Cu-Doped ZnO Hemispherical Shell Structures: Synthesis and Room-Temperature Ferromagnetism Properties [DOI]
  20. 20 Development of a highly transparent, low-resistance lithium-doped nickel oxide triple-layer film deposited by magnetron sputtering [DOI]
  21. 21 Thermal annealing induced structural and optical properties of Ca doped ZnO nanoparticles [DOI]
  22. 22 Photocatalytic Degradation efficiency of CuXZn1-XO Composite [DOI]
  23. 23 Electrical properties of irradiated PVA film by using ion/electron beam [DOI]
  24. 24 Investigation of Annealing Temperature on Copper Oxide Thin Films Using Sol-Gel Spin Coating Technique [DOI]
  25. 25 Electrical conductivity of Cu/ZnO/Si heterostructures [DOI]

Cited by 1

Structural and optical characteristic of 1-(4-Methylsulfonyl Phenyl)-3-(4-n, n Dimethyl (amino Phenyl)-2-Propen- 1-One (MSPPP) Chalcone doped ZnO nanoparticles

Mohana Faroug Attia, Abdelrahman A. Elbadawi · NanoNEXT · 2021

Related research

Article metrics

Real usage data collected on this platform.

38

Page views

0

PDF downloads

4

Outbound clicks

1

Citations

Views over time

Views by country

Approximate, from request IP at view time — not citizenship or institution. Countries with fewer than 5 views are grouped as "Other".

Traffic sources

Referring site, by host.

Views and downloads exclude known bots/crawlers. Citations combines this platform's own DOI-resolved index with each external source's own reported total — see Cited by above for individually listed citing works. Last refreshed 0 seconds ago.